AKROMID®

C3 GF 35 5 XTC black (5552)

PA66+PA6 GF35

AKROMID® C3 GF 35 5 XTC black (5552) is a 35% glass fibre reinforced, high heat stabilised polyamid 66/6 blend with high stiffness and strength and with extra high temperature tolerance.

Modulus

11.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® C3 GF 35 5 XTC black (5552) is a 35% glass fibre reinforced, high heat stabilised polyamid 66/6 blend with high stiffness and strength and with extra high temperature tolerance.

AKROLOY®

PA ICF 30 black (5269)

PA66+PA6I/6T CF30

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

25.000MPa

Strength

220MPa

Impact

50kJ/m²

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

B28 LGF 40 1 L black (6155)

PA6 + PP LGF40

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

Modulus

12.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

AKROMID®

B28 GF 30 9 natural (6614)

PA6 GF30

AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry

AKROMID®

T5 GF 40 black (6486)

PPA GF40

AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

14.500MPa

Strength

245MPa

Impact

80kJ/m²

AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROMID®

B28 GF 50 9 natural (6570)

PA6 GF50

AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release

Modulus

17.000MPa

Strength

250MPa

Impact

115kJ/m²

AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release

PRECITE®

Preliminary

P3 natural (7009)

PBT

PRECITE® P3 natural (7009) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE® P3 natural (7009) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

119202180

AKROMID®

Internal

B3 GF 50 9 RM-M black (3147)PA6 + X GF50

AKROMID® B3 GF 50 9 RM-M black (3147) is a 50% glass fibre reinforced and process improved polyamide 6 with very high rigidity and strength and limited moisture absorption

Features

reduced moisture
process improved

Properties

Modulus

17.500MPa

Strength

215MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17500 MPa
13000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
215 MPa
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
17200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
330 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
70 kJ/m²
70 kJ/m²
60 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
20 kJ/m²
20 kJ/m²
16 kJ/m²
20 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
280 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
165 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,61 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more