HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROTEKĀ®

Preliminary

PK-VM GF 15 black (8686)

PK GF15

AKROTEKĀ® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

4.500MPa

Strength

90MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

UL

C3 GF 25 1 FR natural (7208)

PA66+PA6 GF25 FR(40)

AKROMIDĀ® C3 GF 25 1 FR natural (7208) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

Modulus

9.200MPa

Strength

140MPa

Impact

73kJ/mĀ²

AKROMIDĀ® C3 GF 25 1 FR natural (7208) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

PRECITEĀ®

Preliminary

P3 GF 30 4 LA black (8286)

PBT-I GF30

PRECITEĀ®P3 GF 30 4 LA black (8286) PBT, 30% GF, hydrolysis stabilised, laser markable high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability, light black

Modulus

9.100MPa

Strength

120MPa

Impact

70kJ/mĀ²

PRECITEĀ®P3 GF 30 4 LA black (8286) PBT, 30% GF, hydrolysis stabilised, laser markable high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability, light black

AKROMIDĀ®

UL
Preliminary

C3 GF 30 1 FR grey (8384)

PA66+PA6 GF30 FR(40)

AKROMIDĀ® C3 GF 30 1 FR grey (8384) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 7035, E&E, Public transportation EN 45545-2.

Modulus

10.000MPa

Strength

121MPa

Impact

46kJ/mĀ²

AKROMIDĀ® C3 GF 30 1 FR grey (8384) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 7035, E&E, Public transportation EN 45545-2.

AKROLOYĀ®

UL

PA GF 50 HU black (8198)

PA66+PA6I/6T GF50

AKROLOYĀ® PA GF 50 HU black (8198) is an UL listed, 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

17.000MPa

Strength

265MPa

Impact

105kJ/mĀ²

AKROLOYĀ® PA GF 50 HU black (8198) is an UL listed, 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMIDĀ®

UL

C3 GF 25 1 FR black (7246)

PA66+PA6 GF25 FR(40)

AKROMIDĀ® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

Modulus

9.100MPa

Strength

137MPa

Impact

66kJ/mĀ²

AKROMIDĀ® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

AKROMIDĀ®

UL

C3 GF 30 1 FR white (7630)

PA6+PA66 GF30 FR(40)

AKROMIDĀ® C3 GF 30 1 FR white (7630) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 9016, E&E, Public transportation EN 45545-2.

Modulus

10.600MPa

Strength

140MPa

Impact

NA

AKROMIDĀ® C3 GF 30 1 FR white (7630) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 9016, E&E, Public transportation EN 45545-2.

123480

PRECITEĀ®

Preliminary

P3 GF 50 7 natural (7866)PBT GF 50

PRECITEĀ® P3 GF 50 7 natur (7866) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Properties

Modulus

15.800MPa

Strength

165MPa

Impact

75kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
15800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
165 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
75 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
15 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
212 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 Ā°C

Vicat softening temperature B50

ISO 306

50Ā°C/50N
214 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23Ā°C
1,66 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more