AKROMID®
B3 GF 60 4 RM-M natural (4645)
PA6 + X GF60
AKROMID® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.
21.500MPa
235MPa
65kJ/m²
AKROMID® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.
AKROMID®
B3 GF 60 4 RM-M black (5238)
PA6+X GF60
AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.
22.500MPa
225MPa
60kJ/m²
AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.
AKROLOY®
PA ICF 30 black (5269)
PA66+PA6I/6T CF30
AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
25.000MPa
220MPa
50kJ/m²
AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROMID®
T5 GF 40 black (6486)
PPA GF40
AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
14.500MPa
245MPa
80kJ/m²
AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
AKROMID®
B28 GF 50 9 natural (6570)
PA6 GF50
AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release
17.000MPa
250MPa
115kJ/m²
AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release
AKROMID®
A3 GF 30 4 6 black (13690)
PA66 GF30
AKROMID® A3 GF 30 4 6 black (13690) - PA6.6, 30% glass fiber, cooling water, hydrolysis resistant, DPPD free
10.000MPa
190MPa
85kJ/m²
AKROMID® A3 GF 30 4 6 black (13690) - PA6.6, 30% glass fiber, cooling water, hydrolysis resistant, DPPD free
PRECITE®
P1 GF 30 natural (7062)
PBT GF30
PRECITE® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
9.800MPa
150MPa
75kJ/m²
PRECITE® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
AKROTEK®
PK-VM GF 50 8 natural (6989)PK GF50
AKROTEK® PK-VM GF 50 8 natural (6989) is a 15% glass fibre reinforced polyketone with very high stiffness and strength. PK is characterized by its outstanding media resistance, which qualifies it to be used for components that are in contact with chemicals. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances. Please note that the material is NOT suitable anymore for drinking water contact and does NOT meet the requirements according to KTW, DVGW W270, ACS, WRAS as well as NSF61.
Features
Regulatory
Properties
14.000MPa
160MPa
60kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.