AKROMID®

B3 GF 45 1 black (5744)

PA6 GF45

AKROMID® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.000MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

AKROMID®

A3 GF 40 1 LT black (5709)

PA66 GF40

AKROMID® A3 GF 40 1 LT black (5709) - 40% glass fiber reinforced PA 6.6, heat stabilised, laser transparent, for laser weldable components in the automotive and electronics industry

Modulus

13.000MPa

Strength

225MPa

Impact

100kJ/m²

AKROMID® A3 GF 40 1 LT black (5709) - 40% glass fiber reinforced PA 6.6, heat stabilised, laser transparent, for laser weldable components in the automotive and electronics industry

AKROMID®

UL

A3 GF 50 HU grey (6601)

PA66 GF50

AKROMID® A3 GF 50 HU grey (6601) - 50% glass fiber reinforced PA 6.6, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

255MPa

Impact

110kJ/m²

AKROMID® A3 GF 50 HU grey (6601) - 50% glass fiber reinforced PA 6.6, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and automotive industry

AKROMID®

B28 GF 33 1 GIT black (6846)

PA6 GF33

AKROMID® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.

Modulus

10.500MPa

Strength

190MPa

Impact

95kJ/m²

AKROMID® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.

PRECITE®

Preliminary

E GF 50 natural (7300)

PET GF50

PRECITE® E GF 50 natural (7300) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

18.100MPa

Strength

220MPa

Impact

70kJ/m²

PRECITE® E GF 50 natural (7300) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

C28 GFM 10/20 5 XTC black (7367)

PA66+PA6 (GF10+MD20)

AKROMID® C28 GFM 10/20 5 XTC black (7367) - 10% glass fiber and 20% mineral reinforced, easy flowing and high heat stabilised, high dimensional stability

Modulus

9.500MPa

Strength

120MPa

Impact

40kJ/m²

AKROMID® C28 GFM 10/20 5 XTC black (7367) - 10% glass fiber and 20% mineral reinforced, easy flowing and high heat stabilised, high dimensional stability

PRECITE®

Preliminary

E GF 30 LA black (7825)

PET GF 30

PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.

Modulus

10.500MPa

Strength

155MPa

Impact

45kJ/m²

PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.

116171880

AKROMID®

Internal

A28 GF 50 9 black (5030)PA66 GF50

AKROMID® A28 GF 50 9 black (5030) is a 50% glass fibre reinforced, heat stabilized, process improved, easy flowing polyamide 6.6 with very high stiffness and strength

Features

heat stabilised 130
electrically neutral
surface modified
easy flow
process improved

Properties

Modulus

16.000MPa

Strength

250MPa

Impact

100kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
16000 MPa
12000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
180 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
15200 MPa
13600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
380 MPa
310 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
105 kJ/m²
80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
19 kJ/m²
23 kJ/m²
16 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
290 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
235 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,17 10⁻⁴/K
0,88 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 °C
130 - 150 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,57 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,3 - 1,5 %

Water absorption

ISO 62

23°C, saturated
3,7 - 4,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
1,2 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
220 mm
450 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more