Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

Preliminary

T5 GF 35 6 black (8004)

PPA GF35

AKROMIDĀ® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance


Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/mĀ²

AKROMIDĀ® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

AKROMIDĀ®

C28 GF 25 FRT grey (7560)

PA-Blend

AKROMIDĀ® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.


Modulus

11.000MPa

Strength

135MPa

Impact

60kJ/mĀ²

AKROMIDĀ® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

AKROLOYĀ®

Preliminary

PARA FGF 50 1 black (8186)

PARA FGF50

AKROLOYĀ® PARA FGF 50 1 black (8186) - polyarylamide, 50% flat glass fiber reinforced, improved properties 90Ā° to the flow direction, easy flowing


Modulus

19.000MPa

Strength

295MPa

Impact

75kJ/mĀ²

AKROLOYĀ® PARA FGF 50 1 black (8186) - polyarylamide, 50% flat glass fiber reinforced, improved properties 90Ā° to the flow direction, easy flowing

AKROMIDĀ®

B3 GF 30 1 L black (4365)

PA6+PP GF30

AKROMIDĀ® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride


Modulus

8.800MPa

Strength

140MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

AKROMIDĀ®

B3 GF 50 black (4907)

PA6 GF50

AKROMIDĀ® B3 GF 50 black (4907) - PA6.6, 50% glass fiber, easy flow, high rigidity and strength


Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 50 black (4907) - PA6.6, 50% glass fiber, easy flow, high rigidity and strength

AKROMIDĀ®

A28 GF 50 1 GIT black (5029)

PA66 GF50

AKROMIDĀ® A28 GF 50 1 GIT black (5029) - 50% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface


Modulus

17.500MPa

Strength

270MPa

Impact

100kJ/mĀ²

AKROMIDĀ® A28 GF 50 1 GIT black (5029) - 50% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

AKROMIDĀ®

B3 GF 45 1 black (5744)

PA6 GF45

AKROMIDĀ® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength


Modulus

14.000MPa

Strength

200MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

115161780

AKROTEKĀ®

Preliminary
Internal

PK-VM GF 30 LT black (8653)PK GF30

AKROTEKĀ® PK-VM GF 30 LT black (8653) is a 30% glass fibre reinforced, lasertransparent low viscous polyketone with high stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. This type was developed as the successor to PK-VM GF 30 LT black (8530) und PK-VM GF 30 LT black (6934) in order to meet the requirements for a larger processing window during processing.

Features

hydrolysis / chemically stabilised
laser transparent

Properties

Modulus

8.300MPa

Strength

130MPa

Impact

65kJ/mĀ²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
130 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
210 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
65 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
15 kJ/mĀ²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

General properties


Density

ISO 1183

23Ā°C
1,48 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,6 - 0,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,8 - 1,0 %

Rheological Properties


MVR

ISO 1133

240Ā°C/2,16kg
4 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.