AKROMID®

B3 GF 50 black (4907)

PA6 GF50

AKROMID® B3 GF 50 black (4907) - PA6.6, 50% glass fiber, easy flow, high rigidity and strength

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (4907) - PA6.6, 50% glass fiber, easy flow, high rigidity and strength

AKROMID®

B28 GF 50 natural (4842)

PA6 GF50

AKROMID® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

Modulus

16.500MPa

Strength

250MPa

Impact

110kJ/m²

AKROMID® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

AKROMID®

A28 GF 50 1 GIT black (5029)

PA66 GF50

AKROMID® A28 GF 50 1 GIT black (5029) - 50% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

Modulus

17.500MPa

Strength

270MPa

Impact

100kJ/m²

AKROMID® A28 GF 50 1 GIT black (5029) - 50% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

AKROMID®

B3 GF 60 4 RM-M black (5238)

PA6+X GF60

AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

Modulus

22.500MPa

Strength

225MPa

Impact

60kJ/m²

AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

AKROMID®

D3 GF 30 1 LT black (5391)

PA612 GF30

AKROMID® D3 GF 30 1 LT black (5391) - PA 6.12, glass fiber, laser-transparent,connector

Modulus

9.200MPa

Strength

170MPa

Impact

85kJ/m²

AKROMID® D3 GF 30 1 LT black (5391) - PA 6.12, glass fiber, laser-transparent,connector

AKROLOY®

PA ICF 30 black (5269)

PA66+PA6I/6T CF30

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

25.000MPa

Strength

220MPa

Impact

50kJ/m²

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

B3 GF 30 1 EN black (5637)

PA6 GF30

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

115161780

AKROMID®

B3 GF 30 1 PST black (6647)PA6 GF30

AKROMID® B3 GF 30 1 PST schwarz (6647) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and optimized for adhesion to PST (Plasma Seal-Tight®) coatings developed by Plasmatreat®

Features

heat stabilised 130
adhesion modified

Properties

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10300 MPa
6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
270 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
95 kJ/m²
105 kJ/m²
85 kJ/m²
85 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
13 kJ/m²
18 kJ/m²
12 kJ/m²
12 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,16 10⁻⁴/K
0,95 10⁻⁴/K

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 - 2,3 %

Water absorption

ISO 62

23°C, saturated
6,3 - 6,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more