Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

B3 GF 30 1 L black (4365)

PA6+PP GF30

AKROMID® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

Modulus

8.800MPa

Strength

140MPa

Impact

60kJ/m²

AKROMID® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

AKROMID®

B3 GF 60 4 RM-M natural (4645)

PA6 + X GF60

AKROMID® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.

Modulus

21.500MPa

Strength

235MPa

Impact

65kJ/m²

AKROMID® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.

AKROMID®

A3 GF 40 1 LT black (5709)

PA66 GF40

AKROMID® A3 GF 40 1 LT black (5709) - 40% glass fiber reinforced PA 6.6, heat stabilised, laser transparent, for laser weldable components in the automotive and electronics industry

Modulus

13.000MPa

Strength

225MPa

Impact

100kJ/m²

AKROMID® A3 GF 40 1 LT black (5709) - 40% glass fiber reinforced PA 6.6, heat stabilised, laser transparent, for laser weldable components in the automotive and electronics industry

AKROMID®

B3 GF 45 1 black (5744)

PA6 GF45

AKROMID® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.000MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

AKROMID®

B28 GF 50 natural (4842)

PA6 GF50

AKROMID® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

Modulus

16.500MPa

Strength

250MPa

Impact

110kJ/m²

AKROMID® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

AKROMID®

B3 GF 15 1 L black (4670)

PA6+PP GF15

AKROMID® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

5.200MPa

Strength

105MPa

Impact

60kJ/m²

AKROMID® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROLOY®

PA ICF 30 black (5269)

PA66+PA6I/6T CF30

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

25.000MPa

Strength

220MPa

Impact

50kJ/m²

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

114151680

AKROMID®

Internal

B3 GF 50 9 RM-M black (3147)PA6 + X GF50

AKROMID® B3 GF 50 9 RM-M black (3147) is a 50% glass fibre reinforced and process improved polyamide 6 with very high rigidity and strength and limited moisture absorption

Features

reduced moisture
process improved

Properties

Modulus

17.500MPa

Strength

215MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17500 MPa
13000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
215 MPa
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
17200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
330 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
70 kJ/m²
70 kJ/m²
60 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
20 kJ/m²
20 kJ/m²
16 kJ/m²
20 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
280 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
165 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,61 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.