Select your fitting and find the right compound for your intend
AKROMID®
T9 GF 50 black (7601)
PPA GF50
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
A3 GF 30 8 HU natural (8102)
PA66 GF30
AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
10.500MPa
200MPa
75kJ/m²
AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
AKROLOY®
PARA GF 35 FR grey (8200)
PARA GF35 FR(40)
AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.
14.500MPa
190MPa
50kJ/m²
AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.
AKROMID®
C3 GF 35 1 black (4668)
PA66+PA6 GF35
AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
11.500MPa
200MPa
95kJ/m²
AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GF 30 6 black (20009)
PA6 GF30
AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
10.000MPa
180MPa
80kJ/m²
AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROLOY®
PARA GF 35 FR natural (8038)
PARA GF35 FR(40)
AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
14.500MPa
190MPa
50kJ/m²
AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
AKROMID®
T5 GF 35 4 black (7692)
PPA GF35
AKROMID® T5 GF 35 4 black (7692) is a 35% glass fibre reinforced polyphthalamide with inorganic heat stabilization, very high rigidity and strength, designed for hydrolysis resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
13.500MPa
220MPa
70kJ/m²
AKROMID® T5 GF 35 4 black (7692) is a 35% glass fibre reinforced polyphthalamide with inorganic heat stabilization, very high rigidity and strength, designed for hydrolysis resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
AKROMID®
AKROMID® T5 GF 50 9 black (8001) is a 50% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up. This product was optimized and provides a very good surface quality.
Features
Properties
18.500MPa
255MPa
65kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-2
ISO 11357-3
UL 94
ISO 1183
ISO 294-4
AKRO
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.