Description

AKROMID®

A3 CGM 10/20 4 black (5870)

PA66 (CF10+GF20)

AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

Modulus

14.500MPa

Strength

190MPa

Impact

65kJ/m²

AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

AKROLOY®

PA GF 60 black (6418)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

PRECITE®

P3 GFM 20/10 natural (7627)

PBT (GF20+MD10)

PRECITE® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/m²

PRECITE® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

AKROLOY®

Preliminary

PARA GF 35 FR grey (8200)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

AKROMID®

UL
Preliminary

A3 GF 30 8 HU black (8112)

PA66 GF30

AKROMID® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

AKROMID®

C3 GF 35 1 black (4668)

PA66+PA6 GF35

AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 30 1 L natural (4684)

PA6+PP GF30

AKROMID® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

8.500MPa

Strength

150MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

19101180

AKROMID®

Preliminary
Internal

B3 S1 natural (8084)PA6-I

AKROMID® B3 S1 natural (8084) is an unreinforced, impact modified Polyamide 6. The material is characterised by a very high impact strength even at low temperatures and is therefore perfectly suitable for mountings and dowels in the furniture and construction industry as well as parts for sport and leisure. The material has a light inherent color.

Features

impact modified

Properties

Modulus

1.700MPa

Strength

45MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
1700 MPa
540 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
45 MPa
30 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
4,5 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 100 %
> 200 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
1400 MPa
530 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
55 MPa
25 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
75 kJ/m²
> 100 kJ/m²
40 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
52 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,07 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Dielectric strength

IEC 60243

3 mm
20 kV/mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.