Find the right compound
Select your fitting and find the right compound for your intend
AKROMIDĀ®
A3 GM 20/10 4 WIT black (4529)
PA66 (GF20+GB10)
AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage
8.200MPa
175MPa
65kJ/mĀ²
AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage
PRECITEĀ®
P3 GF 30 black (6924)
PBT GF 30
PRECITEĀ® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
10.000MPa
145MPa
68kJ/mĀ²
PRECITEĀ® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
AKROMIDĀ®
B3 GF 30 6 black (20009)
PA6 GF30
AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
10.000MPa
180MPa
80kJ/mĀ²
AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROLOYĀ®
PARA GF 35 FR grey (8200)
PARA GF35 FR(40)
AKROLOYĀ® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.
14.500MPa
190MPa
50kJ/mĀ²
AKROLOYĀ® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.
AKROMIDĀ®
A3 GF 30 8 HU black (8112)
PA66 GF30
AKROMIDĀ® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
10.500MPa
200MPa
75kJ/mĀ²
AKROMIDĀ® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
AKROMIDĀ®
C3 GF 35 1 black (4668)
PA66+PA6 GF35
AKROMIDĀ® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
11.500MPa
200MPa
95kJ/mĀ²
AKROMIDĀ® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
B28 GF 30 natural (4826)
PA6 GF30
AKROMIDĀ® B28 GF 30 natural (4826) - 30% glass fiber reinforced PA 6, easy flowing, technical parts in industrial engineering and automotive industry
9.500MPa
180MPa
90kJ/mĀ²
AKROMIDĀ® B28 GF 30 natural (4826) - 30% glass fiber reinforced PA 6, easy flowing, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
A3 S1 black (1071)PA66-I
AKROMIDĀ® A3 S1 black 950089 (1071) is an unreinforced, impact modified Polyamide 6.6. The material is characterised by a very high impact strength even at low temperatures and therefore perfectly suitable for connecting and fixing systems which are used in the automotive and electro industry and that are exposed to high loading speeds.
Features
Properties
2.000MPa
50MPa
180kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at yield
ISO 527-2
Tensile strain at yield
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Ball indentation hardness
ISO 2039-1
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.