A3 GF 30 9 FR orange (8014)PA66 GF30 FR(40)

AKROMID® A3 GF 30 9 FR orange (8014) is a 30 % glass fibre reinforced, flame-retardant and heat-stabilized PA6.6, coloured in orange similar to RAL 2003. The material is based on a flame retardant system that is free of red phosphorus, halogens, antimony trioxide, PFAS, zinc borate, and melamine.This type has a V0 classification from a wall thickness of 1.6 mm wall thickness and is characterized by high flowability. If UL listing is required, we refer to our AKROMID® C3 GF 30 1 FR orange (7243), which is based on a PA66/PA6 blend, or our AKROMID® B28 GF 30 9 FR orange (7855), which is based on PA6.

Features

heat stabilised 130
electrically neutral
flame retardant
easy flow
process improved
E&E
E-Mobility

Properties

Modulus

10.200MPa

Strength

145MPa

Impact

65kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10200 MPa
6900 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
145 MPa
95 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,7 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
40°C | d.a.m.
-
65 kJ/m²
65 kJ/m²
57 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
246 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
261 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,37 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Electrical Properties

Volume resistivity

IEC 62631-3-1

d.a.m.
1014 Ω x cm

Surface resistivity

IEC 62631-3-2

d.a.m.
1012 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.