Preliminary datasheet

PA6 – Polyamide 6 PA6 GF35 FR(40)

AKROMID® B28 GF 35 9 FR black (8189)

12600 MPa

155 MPa

65 kJ/m²

AKROMID® B28 GF 35 9 FR black (8189) is an UL listed, easy flowing PA6 with 35% glass-fibers and flame retardant free of halogens and red phosporous. The product contains an organic stabilization package and is optimized for use in electronic and electric applications.

Typical applications

circuit breaker and housings in E&E industry.

Regulatory

UL

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 2 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,08%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 220 - 280°C

3 Nozzle temperature 240 - 280°C

4 Melt temperature 240 - 280°C

5 Mold temperature 60 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 30 - 100 bar

Injection speed medium

Screw speed 5 - 10 m/min

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 12600 MPa
    conditioned 8300 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m. 155 MPa
    conditioned 106 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m. 2,5 %
    conditioned 4,1 %

    Flexural modulus (2 mm/min | ISO 178)
    d.a.m. 11800 MPa
    conditioned 9000 MPa

    Flexural strength (2 mm/min | ISO 178)
    d.a.m. 236 MPa
    conditioned 178 MPa

    Flexural strain at break (2 mm/min | ISO 178)
    d.a.m. 2,8 %
    conditioned 3,6 %

    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m. 65 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m. 11 kJ/m²
    conditioned 14 kJ/m²

  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 210 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 220 °C

  • Flammability
    Burning rate (UL 94)
    1,6mm Wall thickness V-0 Class
    3,2mm Wall thickness V-0 Class

    GWFI (IEC 60695-2-12)
    0,8mm Wall thickness 960 °C
    1,6mm Wall thickness 850 °C

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties
    Density (23°C | ISO 1183) 1,47 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,6-1,8 %

    Molding shrinkage (flow | ISO 294-4) 0,1-0,3 %

    Molding shrinkage (transverse | ISO 294-4) 0,5-0,7 %

  • Electrical Properties
    Comparative tracking index (Test liquid A | IEC 60112) >600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.