Preliminary datasheet

PK – Polyketone PK

AKROTEK® PK-VM 8 black (7810)

1700 MPa


AKROTEK® PK-VM 8 black (7810) is an unreinforced, low viscous polyketone. The material is suitable for food contact and corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR.

Typical applications

Technical and tribological components with high demands on chemiccal resistance as well as friction and wear behaviour.


EU10-2011 FDA

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.

6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 220 - 250°C

3 Nozzle temperature 230 - 250°C

4 Melt temperature 230 - 250°C

5 Mold temperature 60 - 120°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 30 - 70 bar

Injection speed medium to high

Screw speed 8 - 15 m/min


The molding machine needs to be purged with polyolefines before and after processing of AKROTEK® PK! There is a risk of cross linking caused by reactions with POM or PA as well as unsuitable master batches! Cross linking is visible through dark spots! In this case purge immediately with polyolefines.

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 1700 MPa
    conditioned 1700 MPa

    Stress at yield (50 mm/min | ISO 527-2)
    d.a.m. 64 MPa
    conditioned 64 MPa

    Strain at break (50 mm/min | ISO 527-2)
    d.a.m. > 100 %
    conditioned >100 %

    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m. n.b.
    conditioned n.b.

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m. 10 kJ/m²
    conditioned 10 kJ/m²

  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 100 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 220 °C

  • Flammability
    Burning rate (UL 94)
    1,6mm Wall thickness HB Class

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties
    Density (23°C | ISO 1183) 1,24 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 0,8 - 0,9 %

    Molding shrinkage (flow | ISO 294-4) 1,4-1,6 %

    Molding shrinkage (transverse | ISO 294-4) 1,5-1,7 %

  • Electrical Properties
    Volume resistivity (IEC 60093)
    d.a.m. 1,0E+13 Ohm x cm

    Surface resistivity (acc. to IEC 60093)
    d.a.m. 1,0E+13 Ohm

  • Rheological Properties
    MVR (240°C/2,16kg | ISO 1133) 50 cm³/10min


All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.