PA6 – Polyamide 6 PA6 GF35
AKROMID® B3 GF 35 6 black (7605)
AKROMID® B3 GF 35 6 black (7605) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyamide 6 with high rigidity and strength.
Components in mechanical engineering and in the automotive industry.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||240 - 290°C|
|Nozzle temperature||260 - 300°C|
|Melt temperature||270 - 290°C|
|Mold temperature||80 - 100°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 11000 MPa conditioned 6000 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 180 MPa conditioned 105 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,7 % conditioned 5,2 %
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 85 kJ/m² conditioned 95 kJ/m²
Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 75 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 15 kJ/m² conditioned 19 kJ/m²
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 215 °C
Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 220 °C
Burning rate (UL 94) 0,8mm Wall thickness HB Class
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
Density (23°C | ISO 1183) 1,4 g/cm³
Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,8 - 2,1 %
Molding shrinkage (flow | ISO 294-4) 0,1 - 0,3 %
Molding shrinkage (transverse | ISO 294-4) 0,5 - 0,7 %
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.