PARA – Polyarylamide PARA GF 35 FR (40)
AKROLOY® PARA GF 35 FR black (7496)
AKROLOY PARA GF 35 FR black (7496) is a halogen free flame-retarded, 35% glass-fiber reinforced Polyarylamide with very high flow, highest modulus and strength and low
creep. Small water-absorption and very small change of properties due to water-absorption.
Components in Electrical Industry which need low creep even in conditioned state.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||4 - 12 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,08%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||240 - 270°C|
|Melt temperature||240 - 280°C|
|Mold temperature||120 - 160°C|
|Holding pressure, spec.||300-800 bar|
|Back pressure, spec.||30-100 bar|
|Injection speed||medium to high|
|Screw speed||5 - 10 m/min|
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 14600 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 200 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,2 %
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 55 kJ/m²
Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 51 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 13 kJ/m²
Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 14 kJ/m²
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 230 °C
Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 235 °C
Burning rate (UL 94) 0,4mm Wall thickness V-0 Class 0,8mm Wall thickness V-0 Class 1,6mm Wall thickness V-0 Class 3,2mm Wall thickness V-0 Class
GWFI (IEC 60695-2-12) 0,4mm Wall thickness 960 °C 0,8mm Wall thickness 960 °C 1,6mm Wall thickness 960 °C 3,2mm Wall thickness 960 °C
GWIT (IEC 60695-2-13) 0,4mm Wall thickness 825 °C 0,8mm Wall thickness 800 °C 1,6mm Wall thickness 800 °C 3,2mm Wall thickness 825 °C
Density (23°C | ISO 1183) 1,48 g/cm³
Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,4-1,6 %
Molding shrinkage (flow | ISO 294-4) 0,2-0,4 %
Molding shrinkage (transverse | ISO 294-4) 0,4-0,6 %
Comparative tracking index (Test liquid A | IEC 60112) > 600 V
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.