PARA – Polyarylamide PARA CF40
AKROLOY® PARA ICF 40 black (6129)
AKROLOY® PARA ICF 40 black (6129) is a 40% carbon fibre reinforced polyarylamid with good flexural strength, improved processing stabilization versus (6128) and good tribological properties.
Components with high dimensional stability, independent from moisture content.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||4 - 12 h|
|Drying temperature (τ ≤ -30°C)||80 - 90°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||250 - 300°C|
|Nozzle temperature||270 - 300°C|
|Melt temperature||270 - 300°C|
|Mold temperature||120 - 160°C|
|Holding pressure, spec.||300 - 1500 bar|
|Back pressure, spec.||50 - 150 bar|
|Screw speed||8 - 10 m/min|
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 38000 MPa conditioned 37000 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 260 MPa conditioned 250 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 1,0 % conditioned 1,0 %
Flexural modulus (2 mm/min | ISO 178) d.a.m. 37000 MPa conditioned 35000 MPa
Flexural strength (2 mm/min | ISO 178) d.a.m. 420 MPa conditioned 360 MPa
Flexural strain at break (2 mm/min | ISO 178) d.a.m. 1,2 % conditioned 1,1 %
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 35 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 7 kJ/m²
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 230 °C
Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 235 °C
Burning rate (UL 94) 1,6mm Wall thickness HB Class
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
Density (23°C | ISO 1183) 1,4 g/cm³
Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,02 %
Molding shrinkage (flow | ISO 294-4) 0,1 - 0,2 %
Molding shrinkage (transverse | ISO 294-4) 0,2 - 0,4 %
Surface resistivity (acc. to IEC 60093) d.a.m. 1,0E+4 Ohm conditioned 1,0E+4 Ohm
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.