AKROLOY®
PARA FGF 50 1 black (8186)PARA FGF50
AKROLOY® PARA FGF 50 1 black (8186) is a 50% flat glass fiber reinforced polyarylamide. Due to the flat glass fiber, the material is characterised by significantly improved properties 90° to the flow direction as well as low warpage. Even in conditioned state, it impresses with very high stiffness and strength owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys.
Features
Properties
19.000MPa
295MPa
75kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
General properties
Density
ISO 1183
Documents
Discover all the technical specifications at a single glance here.
Processing information
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problem and surface defects.
Drying time
4 - 12 h
Drying temperature (τ ≤ -30°C)
80 - 90 °C
Processing moisture
0,02 - 0,1 %
Feed section
60 - 80 °C
Temperature Zone 1 - Zone 4
250 - 300 °C
Nozzle temperature
270 - 300 °C
Melt temperature
270 - 300 °C
Mold temperature
120 - 160 °C
Holding pressure, spec.
300 - 1500 bar
Back pressure, spec.
50 -150 bar
Injection speed
high
Screw speed
8 - 10 m/min
Applications
Explore more exciting application examples that illustrate how our products can be beneficial to you in various situations and industries.
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.