PRECITE®

P3 GFM 20/10 natural (7627)PBT (GF20+MD10)

PRECITE® P3 GFM 20/10 natural (7627) is a 20% glass fibre reinforced and 10% mineral filled polybutylene terephthalate (PBT) with good surface. Due to its low moisture absorption, this material has very good dimensional stability. It is particularly suitable for precision parts in the automotive, E&E or appliances industry.

Features

surface modified
low warpage
reduced moisture
E&E

Properties

Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
9300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
115 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
7 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,53 g/cm³

Rheological Properties


MVR

ISO 1133

250°C/2,16kg
10 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.