AKROMID®

A3 GF 40 2 L black (7500)PA66+PP GF40

AKROMID® A3 GF 40 2 L black (7500) is a PA6.6-PP-blend with reduced density compared to standard PA66 GF 40. With 40% glass fibre reinforcement, the material is suitable for components with very high strength and stiffness where cost and weight reduction are required at the same time. The materials very good surface quality as well as the outstanding UV-stability make it the product of your choice for technical parts which are exposed to UV radiation. This grade can be used for fuel filters.

Features

heat stabilised 130
surface modified
reduced density

Properties

Modulus

10.600MPa

Strength

150MPa

Impact

70kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10600 MPa
7800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
150 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,8 %
3,7 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
15 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

General properties


Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,9 - 1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,4 - 0,6 %
0,8 - 1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.