E ICF 30 black (7429)PET CF30

PRECITE® E ICF 30 black (7429) is medium viscosity polyethylene terephthalate (PET) with 30% recycled carbon fiber. Despite lower density compared to PET with glass fiber reinforcement, the product has very high strength and toughness as well as high dimensional stability. The good tribological properties and improved surface finish make it the material of choice for precision components in the automotive, mechanical engineering, E&E and household goods industries.

Features

recycled content
surface modified
reduced density
reduced moisture
E&E
Sports & leisure
lightweight construction

Properties

Modulus

24.000MPa

Strength

220MPa

Impact

44kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
24000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
1,9 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
24500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
325 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
44 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
6 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
250 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,05 10⁻⁴/K
0,73 10⁻⁴/K

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,45 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
< 103 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
< 103 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.