AKROMID®

B28 GF 33 1 GIT black (6846)PA6 GF33

AKROMID® B28 GF 33 1 GIT black (6846) is a 33% glass fibre reinforced, heat stabilised polyamide 6. It is characterised by high stiffness and strength. Furthermore, the material impresses with its good processability for gas injection technology and very good surface properties. Therefore it is perfectly suitable for parts in the furniture industry, with high demands on the surface. is therefore perfectly suitable for housings and covers in the automotive industry with high demands on the surface. easy flowing polyamide 6 with very high stiffness and strength for

Features

heat stabilised 130
surface modified
fluid injection (GIT/WIT/FIT)

Properties

Modulus

10.500MPa

Strength

190MPa

Impact

95kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10500 MPa
6600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
190 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
9000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
275 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
95 kJ/m²
105 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
14 kJ/m²
18 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,38 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties


MVR

ISO 1133

275°C/5kg
40 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.