A3 2 S1 grey (5972)PA66-I

AKROMID® A3 2 S1 grey (5972) is an unreinforced, impact modified PA 6.6. The material is UV-stabilised and characterised by a very high cold impact strength. Therefore, it is perfectly suitable for connecting and fixing systems which are used in the automotive, electro and furniture industry where a very high impact strength even at low temperatures is required. The color is similar to RAL 7042.

Features

UV-stabilised
impact modified

Properties

Modulus

1.800MPa

Strength

45MPa

Impact

Na

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1800 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
> 50 %

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
87 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.