AKROMID®

A3 1 S3 black (1139)PA66-I

AKROMID® A3 1 S3 black (1139) is an unreinforced, impact modified Polyamide 6.6. It is characterised by a medium dry impact strength whilst maintaining good flowability. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry. Its good flowability qualifies the material for processing in multi-cavity moulds. For new projects, please consider our successor grade A3 1 S3 schwarz (11392).

Features

heat stabilised 130
impact modified

Properties

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2700 MPa
1300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
63 MPa
45 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
5,6 %
> 20 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 35 %
> 100 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
90 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
7,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
17 kJ/m²
95 kJ/m²
10 kJ/m²
13 kJ/m²

Izod notched impact strength

ISO 180/1A

23°C | d.a.m.
20°C | d.a.m.
-
40°C | d.a.m.
-
15 kJ/m²
12 kJ/m²
12 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
213 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,87 10⁻⁴/K
0,87 10⁻⁴/K

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,0 - 2,2 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Electrical Properties


Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1014

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.