PARA – Polyarylamide PARA GF40
AKROLOY® PARA GF 40 HU natural (8512)AKROLOY® PARA GF 40 HU natural (8512) is a 40% glass fibre reinforced polyarylamid with very high stiffness and strength, even in conditioned state it impresses with very high stiffness and strength owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material is listed at UL in all colors.
Properties
Tensile Modulus Tensile Strength Impact StrengthFeatures
Regulatory
-
Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 15000 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 255 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,3 %
-
Thermal Properties
RTI electrical 0,8mm Wall thickness (UL 746B) 65 °C
RTI electrical 1,6mm Wall thickness (UL 746B) 65 °C
RTI electrical 3,2mm Wall thickness (UL 746B) 65 °C
RTI impact 0,8mm Wall thickness (UL 746B) 65 °C
RTI impact 1,6mm Wall thickness (UL 746B) 65 °C
RTI impact 3,2mm Wall thickness (UL 746B) 65 °C
RTI strength 0,8mm Wall thickness (UL 746B) 65 °C
RTI strength 1,6mm Wall thickness (UL 746B) 65 °C
RTI strength 3,2mm Wall thickness (UL 746B) 65 °C
Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 238 °C
-
Flammability
Burning rate (UL 94) 0,8mm Wall thickness HB Class 1,6mm Wall thickness HB Class 3,2mm Wall thickness HB Class
HWI (UL 746A) 0,8mm Wall thickness 4 PLC 1,6mm Wall thickness 2 PLC 3,2mm Wall thickness 2 PLC
HAI (UL 746A) 0,8mm Wall thickness 0 PLC 1,6mm Wall thickness 0 PLC 3,2mm Wall thickness 0 PLC
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
-
General properties
-
Electrical Properties
Comparative tracking index (Test liquid A | IEC 60112) >600 V
Processing information
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
 |
Drying time | 4 - 12 h |
| Drying temperature (τ ≤ -30°C) | 80 - 90°C | |
| Processing moisture | 0,02 - 0,1% | |
 |
Feed section | 60 - 80°C |
 |
Temperature zone 1 - Zone 4 | 250 - 300°C |
 |
Nozzle temperature | 270 - 300°C |
 |
Melt temperature | 270 - 300°C |
 |
Mold temperature | 120 - 160°C |
 |
Holding pressure, spec. | 300 - 1500 bar |
 |
Back pressure, spec. | 50 -150 bar |
| Injection speed | high | |
| Screw speed | 8 - 10 m/min | |
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.