PA5.6 – Polyamide 5.6 PA56 GF30AKROMID® NEXT 5.6 3 GF 30 S3 black (8444)
The partly bio-based AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) is a HMD-free (hexamethylenediamine) alternative to PA 6.6.
The dry-impact modified PA 5.6 with 30% glass fibre reinforcement is suitable for components with requirements on high strength and stiffness.
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 8600 MPa conditioned 5700 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 180 MPa conditioned 115 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 3,5 % conditioned 8 %
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 96 kJ/m² conditioned 98 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 15 kJ/m² conditioned 22 kJ/m²
Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 254 °C
Biobased carbon content info_outline (calculated) 35 %
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||260 - 300°C|
|Nozzle temperature||270 - 310°C|
|Melt temperature||280 - 300°C|
|Mold temperature||80 - 100°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.