Preliminary datasheet

PA5.10 – Polyamide 5.10 PA5.10 GF30

AKROMID® NEXT 5.10 3 GF 30 natural (8406)

The biobased AKROMID® NEXT 5.10 3 GF 30 natural (8406) is a HMD-free (hexamethylenediamine) alternative to PA 6.10. With 30% glass fibre reinforcement, the material is suitable for components with high strength requirements.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

sustainable
heat stabilised 130
electrically neutral
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 8300 MPa
    conditioned 6000 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 160 MPa
    conditioned 120 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 3,2 %
    conditioned 4,5 %

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 72 kJ/m²
    conditioned 74 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 13 kJ/m²
    conditioned 14 kJ/m²

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 194 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 217 °C

  • General properties

    Density (23°C | ISO 1183) 1,29 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,2 %

  • Sustainability

    Biobased carbon content info_outline (calculated) 97 %

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 240 - 290°C

3 Nozzle temperature 260 - 300°C

4 Melt temperature 270 - 290°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Application examples

AKROMID® NEXT - innovative and sustainable solutions

 

More about AKROMID® NEXT