AKROLOY®

Preliminary

PARA GF 50 8 black (8394)PARA GF50

AKROLOY® PARA GF 50 8 black (8394) is a 50% glass fibre reinforced polyarylamid with very high stiffness and strength. Even in conditioned state, it impresses with very high stiffness and strength owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances.

Features

easy flow

Regulatory

eu102011fda

Properties

Modulus

20.000MPa

Strength

290MPa

Impact

74kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
290 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
1,9 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
74 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
18 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

General properties

Density

ISO 1183

23°C
1,65 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,0 - 0,2 %
0,2 - 0,4 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.