AKROMID® B28 GF 30 S3 natural (8348)

AKROMID® B28 GF 30 S3 natural (8348) is a 30% glass fibre reinforced, easy flowing polyamide 6. Furthermore, the material is impact modified and therefore characterised by a higher dry impact strength compared to standard PA 6 GF 30. Its high strength and stiffness make it the material of your choice for technical applications in industrial engineering and in the furniture industry. The material has a light inherent color.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

impact modified
easy flow
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 8900 MPa
    conditioned 5000 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 160 MPa
    conditioned 105 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 4,5 %
    conditioned 10 %

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 100 kJ/m²
    conditioned 100 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 15 kJ/m²
    conditioned 30 kJ/m²

  • Thermal Properties

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 220 °C

  • Flammability

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties

    Density (23°C | ISO 1183) 1,3 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 2,1 %

    Molding shrinkage (flow | ISO 294-4) 0,1 - 0,3 %

    Molding shrinkage (transverse | ISO 294-4) 0,5 - 0,7 %

  • Rheological Properties

    MVR (275°C/5kg | ISO 1133) 35 cm³/10min

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 240 - 290°C

3 Nozzle temperature 260 - 300°C

4 Melt temperature 270 - 290°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.