PA6.6/6 – Polyamide 6.6/6 PA66 + PA6-I
AKROMID® A3 1 S3 black (8341)AKROMID® A3 1 S3 black (8341) is an unreinforced, impact modified Polyamide 6.6. It is characterised by a medium dry impact strength whilst maintaining good flowability. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry. Its good flowability qualifies the material for processing in multi-cavity moulds.
Properties
Tensile Modulus Tensile Strength Impact StrengthFeatures
-
Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 2500 MPa conditioned 1000 MPa
Stress at yield (50 mm/min | ISO 527-2) d.a.m. 60 MPa conditioned 40 MPa
Strain at yield (50 mm/min | ISO 527-2) d.a.m. 8 % conditioned 35 %
Stress at break (50 mm/min | ISO 527-2) d.a.m. 48 MPa conditioned 44 MPa
Strain at break (50 mm/min | ISO 527-2) d.a.m. 32 % conditioned >100 %
Flexural modulus (2 mm/min | ISO 178) d.a.m. 2400 MPa conditioned 1000 MPa
Flexural strength (2 mm/min | ISO 178) d.a.m. 90 MPa conditioned 40 MPa
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. n.b. conditioned n.b.
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 12 kJ/m² conditioned 92 kJ/m²
-
Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 65 °C
Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 175 °C
Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 258 °C
-
Flammability
Burning rate (UL 94) 1,6mm Wall thickness HB Class
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
-
General properties
Density (23°C | ISO 1183) 1,1 g/cm³
Humidity absorption (70°C, 62% r.H. | ISO 1110) 2,4 %
Molding shrinkage (flow | ISO 294-4) 1,3 - 1,5 %
Molding shrinkage (transverse | ISO 294-4) 1,5 - 1,7 %
-
Electrical Properties
Volume resistivity (IEC 60093) d.a.m. 1,0E+15 Ω · cm
Volume resistivity (DIN EN 62631-3-1) d.a.m. 1,0E+15 Ω · cm
Surface resistivity (DIN EN 62631-3-2) d.a.m. 1,0E+14 Ω
Processing information
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
 |
Drying time | 2 - 4 h |
| Drying temperature (τ ≤ -30°C) | 80°C | |
| Processing moisture | 0,02 - 0,1% | |
 |
Feed section | 60 - 80°C |
 |
Temperature zone 1 - Zone 4 | 260 - 300°C |
 |
Nozzle temperature | 270 - 310°C |
 |
Melt temperature | 270 - 300°C |
 |
Mold temperature | 40 - 90°C |
 |
Holding pressure, spec. | 300 - 800 bar |
 |
Back pressure, spec. | 50 - 150 bar |
| Injection speed | medium to high | |
| Screw speed | 8 - 15 m/min | |
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.