PBT – Polybutyleneterephthalate PBT GF 20

PRECITE® P3 GF 20 black (8340)

PRECITE® P3 GF 20 black (8340) is a 20 % glass fibre reinforced, medium viscosity polybutylene terephthalate (PBT) with high stiffness and strength. Due to its low moisture absorption, this material has very good dimensional stability. It is particularly suitable for precision parts in the automotive or E&E industry.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

E&E
industrial
household

  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 7000 MPa
    Stress at break (5 mm/min | ISO 527-2) d.a.m. 120 MPa
    Strain at break (5 mm/min | ISO 527-2) d.a.m. 3,5 %
    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 50 kJ/m²
    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 10 kJ/m²

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 205 °C
    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 225 °C

  • Flammability

    Burning rate (UL 94)
    1,6mm Wall thickness HB Class

  • General properties

    Density (23°C | ISO 1183) 1,45 g/cm³
    Molding shrinkage (flow | ISO 294-4) 0,4 - 0,6 %
    Molding shrinkage (transverse | ISO 294-4) 0,9 - 1,1 %

  • Electrical Properties

    Comparative tracking index (Test liquid A | IEC 60112) 225 V
    Dieletric strength (3 mm | IEC 60243) 33 kV/mm

  • Rheological Properties

    MVR (250°C/2,16kg | ISO 1133) 10 cm³/10min

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
6 Drying time 3 - 4 h
Drying temperature (τ ≤ -30°C) 100 - 120°C
Processing moisture 0,02 - 0,04%
1 Feed section 60 - 80°C
2 Temperature zone 1 - Zone 4 250 - 275°C
3 Nozzle temperature 250 - 280°C
4 Melt temperature 260 - 275°C
5 Mold temperature 80 - 100°C
P Nach Holding pressure, spec. 300 - 800 bar
P Stau Back pressure, spec. 30 - 100 bar
Injection speed medium to high
Screw speed 8 - 15 m/min

Warning

Due to hydrolysis sensitivity of polyesters, a careful drying of the material before processing is very important. High residual moisture contents causes, in addition to surface defects, a decomposition of the molecular chains and thus reduced mechanical properties. If there are longer interruptions of the process, the cylinder temperature should be lowered. Furthermore, we recommend a thorough cleaning of the screw cylinder with extended dwell time or a material change. Glass-fiber-reinforced polyolefins (PE, PP) have established a particularly good cleaning effect.

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.