PA11 – Polyamide 11 PA11 CF30

AKROMID® NEXT U28 ICF 30 1 black (8233)

AKROMID® NEXT U28 ICF 30 1 black (8231) is a 30% carbon fiber reinforced Polyamide 11 which consists of > 97% renewable raw materials based on castor oil. Its low density as well as excellent ductility even at lower temperatures combined with high stiffness and strength enable the use for demanding applications, e.g., for lightweight construction or sports & leisure.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

3D printing/ additive manufacturing
heat stabilised 130
reduced moisture
reduced density
sustainable
recycled content
lightweight construction
sports & leisure
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 15300 MPa
    conditioned 10900 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 165 MPa
    conditioned 140 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 4,8 %
    conditioned 4,8 %

    Flexural modulus (2 mm/min | ISO 178) d.a.m. 15000 MPa
    conditioned 12000 MPa

    Flexural strength (2 mm/min | ISO 178) d.a.m. 260 MPa
    conditioned 220 MPa

    Flexural strain at break (2 mm/min | ISO 178) d.a.m. 3,7 %
    conditioned 4,2 %

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 75 kJ/m²
    conditioned 70 kJ/m²

    Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 70 kJ/m²
    conditioned 65 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 13 kJ/m²
    conditioned 12 kJ/m²

    Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 9 kJ/m²
    conditioned 8 kJ/m²

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 180 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 189 °C

  • General properties

    Density (23°C | ISO 1183) 1,22 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 0,7-0,9 %

    Water absorption 23°C saturated (23°C, saturated | ISO 62) 1,3-1,7 %

    Molding shrinkage (flow | ISO 294-4) 0,3-0,5 %

    Molding shrinkage (transverse | ISO 294-4) 0,7-0,9 %

  • Sustainability

    Biobased carbon content info_outline (calculated) 52 %

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 240 - 300°C

3 Nozzle temperature 230 - 300°C

4 Melt temperature 240 - 290°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.