AKROMID®

UL
Preliminary

B28 GF 35 9 FR black (8189)PA6 GF35 FR(40)

AKROMID® B28 GF 35 9 FR black (8189) is a flame retardant PA6 with 35% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. This grade is UL listed with a V0 classification at 1.6mm. Due to its very good flowability, it is characterised by easy processability as well as good surface properties. The material has excellent long-term thermal stability and outstanding mechanical properties.

Features

heat stabilised 130
electrically neutral
flame retardant
easy flow
E&E
E-Mobility

Regulatory

ul

Properties

Modulus

12.600MPa

Strength

152MPa

Impact

70kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12600 MPa
8300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
152 MPa
108 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,6 %
4,0 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
11800 MPa
9000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
240 MPa
179 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
3,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
70 kJ/m²
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
12 kJ/m²
14 kJ/m²
11 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
211 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
165 °C
135 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
850 °C

HWI

UL 746A

1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC

HAI

UL 746A

1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,46 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,6 - 1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties


Volume resistivity IEC

DIN EN 62631-3-2

d.a.m.
1012 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012

Comparative tracking index

IEC 60112

Test liquid A
600 V

Dielectric strength

IEC 60243

3 mm
22 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

1,5 kV

High voltage arc tracking rate (HVTR)

UL 746A

1 PLC

High Volt, Low Current Arc Resistance

ASTM D495

4 PLC

Rheological Properties


Flowability

AKRO

1 mm Thickness
2 mm Thickness
120 mm
410 mm

MVR

ISO 1133

275°C/5kg
40 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.