Preliminary datasheet

PA6.6 – Polyamide 6.6 PA6.6 GF30

AKROMID® A3 GF 30 6 ECO black (8160)

AKROMID® A3 GF 30 6 ECO black (8160) is a 30% glass fibre-reinforced, inorganically heat-stabilised polyamide 6.6. The material is suitable for technical components in mechanical engineering and the automotive industry with demands for high stiffness and strength. The formulations of the sustainable ECO products are partly based on regenerated post-industrial feedstock and thus contribute to reducing the consumption of valuable raw materials. This type is laser-markable.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

heat stabilised 160
sustainable
laser markable
recycled content
CO₂eq reduced
industrial
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 9000 MPa
    conditioned 6300 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 150 MPa
    conditioned 100 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,5 %
    conditioned 5 %

    Flexural modulus (2 mm/min | ISO 178) d.a.m. 7500 MPa

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 50 kJ/m²
    conditioned 65 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 7 kJ/m²
    conditioned 11 kJ/m²

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 255 °C

    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 260 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 262 °C

  • Flammability

    Burning rate (UL 94)
    1,6mm Wall thickness HB Class

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties

    Density (23°C | ISO 1183) 1,36 g/cm³

    Molding shrinkage (flow | ISO 294-4) 0,1-0,3 %

    Molding shrinkage (transverse | ISO 294-4) 0,5-0,7 %

  • Sustainability

    Recycled content (at least) 30 %

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 260 - 300°C

3 Nozzle temperature 270 - 310°C

4 Melt temperature 280 - 300°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.