Preliminary datasheet

PARA – Polyarylamide PARA GF 35 FR (40)

AKROLOY® PARA GF 35 FR orange (8039)

AKROLOY® PARA GF 35 FR orange (8039) is a flame retardant, 35% glass-fiber reinforced Polyarylamide with highest modulus and strength. The material is based on a flame retardant system that is free of red phosphorus and halogens and is colored in orange similar to RAL 2003. Due to its very good flowability, an improved surface quality is achieved. This grade is also suitable for applications in electrical industries, which need low creep even in conditioned state.


Tensile Modulus
Tensile Strength
Impact Strength


flame retardant
easy flow
electrically neutral
surface modified
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 14700 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 175 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 1,8 %

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 45 kJ/m²

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 230 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 235 °C

  • Flammability

    Burning rate (UL 94)
    0,4mm Wall thickness V-0 Class
    0,8mm Wall thickness V-0 Class
    1,6mm Wall thickness V-0 Class
    3,2mm Wall thickness V-0 Class

    GWFI (IEC 60695-2-12)
    0,4mm Wall thickness 960 °C
    0,8mm Wall thickness 960 °C
    1,6mm Wall thickness 960 °C
    3,2mm Wall thickness 960 °C

    GWIT (IEC 60695-2-13)
    0,4mm Wall thickness 825 °C
    0,8mm Wall thickness 800 °C
    1,6mm Wall thickness 800 °C
    3,2mm Wall thickness 825 °C

  • General properties

    Density (23°C | ISO 1183) 1,48 g/cm³

    Molding shrinkage (flow | ISO 294-4) 0,2-0,4 %

    Molding shrinkage (transverse | ISO 294-4) 0,4-0,6 %

  • Electrical Properties

    Comparative tracking index (Test liquid A | IEC 60112) > 600 V

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.

6 Drying time 4 - 12 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,08%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 240 - 270°C

3 Nozzle temperature 240-280°C

4 Melt temperature 240 - 280°C

5 Mold temperature 120 - 160°C

P Nach Holding pressure, spec. 300-800 bar

P Stau Back pressure, spec. 30-100 bar

Injection speed medium to high

Screw speed 5 - 10 m/min


All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.