Preliminary datasheet

PPA – Polyphthalamide PPA GF30

AKROMID® T5 GF 30 6 black (8006)

AKROMID® T5 GF 30 black (8006) is a 30% glass fibre reinforced polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Typical applications

Applications are parts with tight dimensional tolerances even under high mechanical load.

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 120°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 90°C

2 Temperature zone 1 - Zone 4 320 - 350°C

3 Nozzle temperature 330 - 350°C

4 Melt temperature 330 - 350°C

5 Mold temperature 120 - 160°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 12000 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m. 200 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m. 2,4 %

    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m. 55 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m. 8 kJ/m²

  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 270 °C

    Melting temperature (DSC, 10K/min | DIN EN 11357-1) 325 °C

  • General properties
    Density (23°C | ISO 1183) 1,4 g/cm³

    Molding shrinkage (flow | ISO 294-4) 0,4-0,6 %

    Molding shrinkage (transverse | ISO 294-4) 0,7-0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

You have questions about our products?

With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.

CONTACT US NOW