PA6 – Polyamide 6 PA6 GF60
AKROMID® B28 GF 60 9 black (7967)
AKROMID® B28 GF 60 9 black (7967) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength.
Components in mechanical engineering and the automotive industry.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||240 - 290°C|
|Nozzle temperature||260 - 300°C|
|Melt temperature||270 - 290°C|
|Mold temperature||80 - 100°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 21000 MPa conditioned 13500 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 250 MPa conditioned 160 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,3 % conditioned 3 %
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 90 kJ/m² conditioned 95 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 20 kJ/m² conditioned 25 kJ/m²
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 220 °C
Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 220 °C
Melting temperature (DSC, 10K/min | DIN EN 11357-1) 220 °C
Burning rate (UL 94) 1,6mm Wall thickness HB Class
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
Density (23°C | ISO 1183) 1,7 g/cm³
Humidity absorption (70°C, 62% r.H. | ISO 1110) 0,9 - 1,2 %
Flowability (1mm Thickness | AKRO) 170 mm
Flowability (2mm Thickness | AKRO) 560 mm
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.