PA6 – Polyamide 6 PA6
AKROMID® B3 HU grey (7897)
AKROMID® B3 HU grey (7897) is an at UL listed unreinforced and heat stabilised polyamide 6 colored in light grey (RAL 7035)
Housings, cable glands and fixtures in the automotive and electric industry.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||2 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,08%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||220 - 260°C|
|Nozzle temperature||230 - 270°C|
|Melt temperature||240 - 270°C|
|Mold temperature||60 - 80°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||30 - 100 bar|
|Screw speed||5 - 10 m/min|
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 3400 MPa
Stress at yield (50 mm/min | ISO 527-2) d.a.m. 80 MPa
Strain at break (50 mm/min | ISO 527-2) d.a.m. >10 %
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. n.b.
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 60 °C
Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 180 °C
Melting temperature (DSC, 10K/min | DIN EN 11357-1) 220 °C
Vicat softening temperature B50 (50°C/50N | ISO 306) 202 °C
Burning rate (UL 94) 0,4mm Wall thickness V-2 Class 0,8mm Wall thickness V-2 Class 1,6mm Wall thickness V-2 Class 3,2mm Wall thickness V-2 Class
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
Density (23°C | ISO 1183) 1,13 g/cm³
Molding shrinkage (flow | ISO 294-4) 1,0-1,2 %
Molding shrinkage (transverse | ISO 294-4) 1,1-1,3 %
Comparative tracking index (Test liquid A | IEC 60112) >600 V
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
You have questions about our products?
With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.CONTACT US NOW