Menu Career Language: EN/DE

PPA – Polyphthalamide PPA GF35

AKROMID® T9 GF 35 4 black (7858)

AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance.

 

The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

heat stabilised 160
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 11000 MPa
    conditioned 11000 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 200 MPa
    conditioned 175 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,5 %
    conditioned 2,2 %

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 75 kJ/m²
    conditioned 100 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 12 kJ/m²
    conditioned 16 kJ/m²

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 270 °C

    Glass transition temperature (DSC, 2nd heating | DIN EN ISO 11357-2) 125 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 305 °C

  • Flammability

    Burning rate (UL 94)
    1,6mm Wall thickness HB Class

  • General properties

    Density (23°C | ISO 1183) 1,41 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 0,1-0,3 %

    Molding shrinkage (flow | ISO 294-4) 0,15 - 0,35 %

    Molding shrinkage (transverse | ISO 294-4) 0,55 - 0,75 %

  • Electrical Properties

    Comparative tracking index (Test liquid A | IEC 60112) 600 V

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 120°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 90°C

2 Temperature zone 1 - Zone 4 310 - 340°C

3 Nozzle temperature 320 - 340°C

4 Melt temperature 320 - 340°C

5 Mold temperature 120 - 160°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Measuring Curves