C3 GF 25 1 FR orange (7854)PA66/6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR orange (7854) is a 25 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend, colored in orange similar to RAL 2003. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable for high voltage components in e-mobility.

Features

heat stabilised 130
flame retardant
surface modified
easy flow
E&E

Regulatory

ul

Properties

Modulus

9.000MPa

Strength

126MPa

Impact

61kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
9000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
126 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
61 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
9 kJ/m²

Thermal Properties


RTI electrical

UL 746B

0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
150 °C
150 °C
150 °C

RTI impact

UL 746B

0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
125 °C
125 °C
125 °C

RTI strength

UL 746B

0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
140 °C
140 °C
140 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
155 °C
130 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
750 °C
750 °C
750 °C

HWI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

HAI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,38 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties


Volume resistivity IEC

DIN EN 62631-3-2

d.a.m.
1012 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Dielectric strength

IEC 60243

3 mm
12 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

1 kV

High voltage arc tracking rate (HVTR)

UL 746A

1 PLC

High Volt, Low Current Arc Resistance

ASTM D495

6 PLC

Rheological Properties


Flowability

AKRO

1 mm Thickness
2 mm Thickness
220 mm
480 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.