Preliminary datasheet

PA6 – Polyamide 6 PA6 + PP GF20

AKROMID® B3 GF 20 9 L white (7802)

AKROMID® B3 GF 20 9 L white (7802) is a 20% glass fibre reinforced, process optimised polyamide-blend with a reduced density compared to standard PA6 GF 20, white coloured.

Typical applications

Technical components in the automotive and electronic industry, where a weight reduction is required

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6Drying time0 - 4 h

Drying temperature (τ ≤ -30°C)80°C

Processing moisture0,02 - 0,1%

1Feed section60 - 80°C

2Temperature zone 1 - Zone 4220 - 290°C

3Nozzle temperature240 - 300°C

4Melting temperature240 - 290°C

5Mold temperature70 - 100°C

P NachHolding pressure, spec.300 - 800 bar

P StauBack pressure, spec.50 - 150 bar

Injection speedmedium to high

Screw speed5 - 15 m/min

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m.6500 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m.115 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m.4,0 %

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m.13 kJ/m²

  • Thermal Properties
    Melting temperature (DSC, 10K/min | DIN EN 11357-1)220 °C

  • General properties
    Density (23°C | ISO 1183)1,21 g/cm³

    Humidity absorption (70°C, 62% r.F. | ISO 1110)1,6-1,8 %

  • Rheological Properties
    MVR (275°C/5kg | ISO 1133)21 cm³/10min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

You have questions about our products?

With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.

CONTACT US NOW