AKROMID®

Preliminary

B+ GF 30 6 LT black (7665)PA6 GF30

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Features

heat stabilised 160

Properties

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10000 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
6,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
13 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,36 g/cm³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.