PBT/PET Compound PBT-PET- CF 30

PRECITE® K ICF 30 black (7570)

PRECITE® K ICF 30 black (7570) is a PBT/PET blend with 30% recycled carbon fiber. Despite lower density compared to PBT/PET blends with glass fiber reinforcement, the product has very high strength. The good tribological properties and improved surface finish make it the material of choice for precision components in automotive, mechanical engineering, E&E and household goods industries.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

sustainable
reduced density
reduced moisture
surface modified
recycled content
E&E
sports & leisure
industrial
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 24000 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 190 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,1 %

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 55 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 8 kJ/m²

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 206 °C

  • Flammability

    Burning rate (UL 94)
    0,8mm Wall thickness HB Class

  • General properties

    Density (23°C | ISO 1183) 1,43 g/cm³

  • Sustainability

    Recycled content (at least) 30 %

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 3 - 4 h

Drying temperature (τ ≤ -30°C) 120 - 140°C

Processing moisture ≤ 0,02%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 260 - 280°C

3 Nozzle temperature 260 - 290°C

4 Melt temperature 270 - 280°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 30 - 100 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Warning

Due to hydrolysis sensitivity of polyesters, a careful drying of the material before processing is very important. High residual moisture contents causes, in addition to surface defects, a decomposition of the molecular chains and thus reduced mechanical properties. If there are longer interruptions of the process, the cylinder temperature should be lowered. Furthermore, we recommend a thorough cleaning of the screw cylinder with extended dwell time or a material change. Glass-fiber-reinforced polyolefins (PE, PP) have established a particularly good cleaning effect.

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.