PA6 – Polyamide 6 PA6 + PP GF30

AKROMID® B3 GF 30 4 L black (7481)

AKROMID® B3 GF 30 4 L black (7481) is a PA6/PP-blend with reduced density compared to standard PA6 with 30% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMID® B3 GF 30 4 L black (7481) is particularly superior to water glycol. This compound fulfills the requirements of VW TL52682 (1000h/135°C; 50/50 G12 EVO/water) and can be used for applications that are in contact witch cooling water.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

heat stabilised 130
reduced density
hydrolysis/ chemically stabilised
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 9000 MPa
    conditioned 7000 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 145 MPa
    conditioned 110 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 3,1 %
    conditioned 4,6 %

    Flexural modulus (2 mm/min | ISO 178) d.a.m. 9200 MPa
    conditioned 6500 MPa

    Flexural strength (2 mm/min | ISO 178) d.a.m. 225 MPa
    conditioned 160 MPa

    Flexural strain at break (2 mm/min | ISO 178) d.a.m. 3,4 %
    conditioned 4,3 %

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 70 kJ/m²
    conditioned 65 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 17 kJ/m²
    conditioned 18 kJ/m²

    Ball indentation hardness (358N/30s | ISO 2039-1) d.a.m. 170 MPa

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 200 °C

    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 217 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 220 °C

    Coefficent of linear thermal expansion, parallel (23°C bis 80°C | ISO 11359-1/2) 0,17 1,0E-4/K

    Coefficent of linear thermal expansion, transverse (23°C bis 80°C | ISO 11359-1/2) 1,34 1,0E-4/K

  • Flammability

    Burning rate (UL 94)
    0,8mm Wall thickness HB Class

    GWFI (IEC 60695-2-12)
    0,8mm Wall thickness 650 °C

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties

    Density (23°C | ISO 1183) 1,26 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,3-1,5 %

    Molding shrinkage (flow | ISO 294-4) 0,1 - 0,3 %

    Molding shrinkage (transverse | ISO 294-4) 0,5 - 0,7 %

  • Rheological Properties

    MVR (275°C/5kg | ISO 1133) 14 cm³/10min

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 220 - 290°C

3 Nozzle temperature 240 - 300°C

4 Melt temperature 240 - 290°C

5 Mold temperature 70 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 5 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.