PA6.6/6 – Polyamide 6.6/6 PA66 + PA 6 FR (30)

AKROMID® C3 1 FR orange (7470)

AKROMID® C3 1 FR orange (7470) is an unreinforced, flame retardant and heat stabilised PA6/6.6 blend. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its very good flowability, an improved surface quality is achieved. The material is colored in orange (similar RAL 2003) and suitable for high voltage components in e-mobility.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

flame retardant
heat stabilised 130
easy flow
E&E
industrial

Regulatory

UL
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 3500 MPa
    conditioned 1300 MPa

    Stress at yield (50 mm/min | ISO 527-2) d.a.m. 76 MPa
    conditioned 45 MPa

    Strain at break (50 mm/min | ISO 527-2) d.a.m. >10 %
    conditioned >50 %

    Poisson's ratio (0,05 % - 0,25 % | ISO 527-2) d.a.m. 0,4

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 70 °C

    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 210 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 260 °C

    Temperature index for 50% loss of tensile strength after 5.000h (5.000 h | IEC 60216) 126 °C

    Temperature index for 50% loss of tensile strength after 20.000h (20.000 Std. | IEC 60216) 111 °C

    Thermal conductivity (DIN 52612) 0,34 W/mK

  • Flammability

    Burning rate (UL 94)
    0,4mm Wall thickness V-0 Class
    0,8mm Wall thickness V-0 Class
    1,6mm Wall thickness V-0 Class
    3,2mm Wall thickness V-0 Class

    GWFI (IEC 60695-2-12)
    0,4mm Wall thickness 960 °C
    0,8mm Wall thickness 960 °C
    1,6mm Wall thickness 960 °C
    3,2mm Wall thickness 960 °C

    HWI (UL 746A)
    0,4mm Wall thickness 4 PLC
    0,8mm Wall thickness 4 PLC
    1,6mm Wall thickness 0 PLC
    3,2mm Wall thickness 0 PLC

    HAI (UL 746A)
    0,4mm Wall thickness 0 PLC
    0,8mm Wall thickness 0 PLC
    1,6mm Wall thickness 0 PLC
    3,2mm Wall thickness 0 PLC

    Oxygen index (ISO 4589-2) >32 %

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties

    Density (23°C | ISO 1183) 1,20 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 2,3 %

    Molding shrinkage (flow | ISO 294-4) 1,1-1,3 %

    Molding shrinkage (transverse | ISO 294-4) 1,3-1,5 %

  • Electrical Properties

    Comparative tracking index (Test liquid A | IEC 60112) >600 V

    Dielectric strength (3 mm | IEC 60243) 10 kV/mm

    Inclined-Plane Tracking, IPT (ASTM D2303-13) 1 kV

  • Rheological Properties

    Flowability (1mm Thickness | AKRO) 320 mm

    Flowability (2mm Thickness | AKRO) 640 mm

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 2 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,08%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 260 - 280°C

3 Nozzle temperature 260 - 280°C

4 Melt temperature 260 - 280°C

5 Mold temperature 60 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 30 - 100 bar

Injection speed medium

Screw speed 5 - 10 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.