Preliminary datasheet

PA6 – Polyamide 6 PA6 GF30

AKROMID® B+ GF 30 6 black (7387)

9500 MPa

180 MPa

86 kJ/m²

High-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Typical applications

Components in mechanical engineering and in the automotive industry

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 240 - 290°C

3 Nozzle temperature 260 - 300°C

4 Melt temperature 270 - 290°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 9500 MPa
    conditioned 6000 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m. 180 MPa
    conditioned 118 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m. 3,6 %
    conditioned 9 %

    Flexural modulus (2 mm/min | ISO 178)
    d.a.m. 9200 MPa

    Flexural strength (2 mm/min | ISO 178)
    d.a.m. 270 MPa

    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m. 86 kJ/m²

    Charpy impact strength (-30°C | ISO 179-1/1eU)
    d.a.m. 72 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m. 14 kJ/m²
    conditioned 19 kJ/m²

    Charpy notched impact strength (-30°C | ISO 179-1/1eA)
    d.a.m. 11 kJ/m²
    conditioned 11 kJ/m²

  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 210 °C

    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 218 °C

    Melting temperature (DSC, 10K/min | DIN EN 11357-1) 220 °C

    Coefficent of linear thermal expansion, parallel (23°C bis 80°C | ISO 11359-1/2) 0,19 1,0E-4/K

    Coefficent of linear thermal expansion, transverse (23°C bis 80°C | ISO 11359-1/2) 1,14 1,0E-4/K

  • General properties
    Density (23°C | ISO 1183) 1,35 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,9-2,1 %

    Molding shrinkage (flow | ISO 294-4) 0,1-0,3 %

    Molding shrinkage (transverse | ISO 294-4) 0,5-0,7 %

  • Rheological Properties
    Flowability (2mm Thickness | AKRO) 480 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

You have questions about our products?

With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.

CONTACT US NOW