PBT/PET Compound PBT-PET- GF 30

PRECITE® K GF 30 black (7249)

PRECITE K GF 30 black (7249) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

Typical applications

Precision parts in automobile and E/E industry

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.

6Drying time3 - 4 h

Drying temperature (τ ≤ -30°C)120 - 140°C

Processing moisture≤ 0,02%

1Feed section60 - 80°C

2Temperature zone 1 - Zone 4260 - 280°C

3Nozzle temperature260 - 290°C

4Melting temperature270 - 280°C

5Mold temperature80 - 100°C

P NachHolding pressure, spec.300 - 800 bar

P StauBack pressure, spec.30 - 100 bar

Injection speedmedium to high

Screw speed8 - 15 m/min


Due to hydrolysis sensitivity of polyesters, a careful drying of the material before processing is very important. High residual moisture contents causes, in addition to surface defects, a decomposition of the molecular chains and thus reduced mechanical properties. If there are longer interruptions of the process, the cylinder temperature should be lowered. Furthermore, we recommend a thorough cleaning of the screw cylinder with extended dwell time or a material change. Glass-fiber-reinforced polyolefins (PE, PP) have established a particularly good cleaning effect.

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m.9800 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m.150 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m.3,1 %

    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m.65 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m.10 kJ/m²

  • Flammability
    Burning rate (UL 94)
    0,8mm Wall thicknessHB Class

  • General properties
    Density (23°C | ISO 1183)1,55 g/cm³


All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.