Preliminary datasheet

PA6.6/6 – Polyamide 6.6/6 PA6.6/6 GF30 FR

AKROMID® C3 GF 30 1 FR natural (7207)

10500 MPa

150 MPa

76 kJ/m²

  • 76 kJ/m²

AKROMID® C3 GF 30 1 FR natural (7207) is a 30 % glass fibre reinforced, heat stabilized and halogenfree flame retardant polyamide 6.6/6 - Blend.

Typical applications

Components in mechanical engineering and the automotive industry where good flowability is required

Regulatory

UL

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
6 Drying time 2 - 4 h
Drying temperature (τ ≤ -30°C) 80°C
Processing moisture 0,02 - 0,08%
1 Feed section 60 - 80°C
2 Temperature zone 1 - Zone 4 260 - 290°C
3 Nozzle temperature 260 - 300°C
4 Melt temperature 280 - 290°C
5 Mold temperature 60 - 100°C
P Nach Holding pressure, spec. 300 - 800 bar
P Stau Back pressure, spec. 30 - 100 bar
Injection speed medium
Screw speed 5 - 10 m/min
  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 10500 MPa
    Stress at break (5 mm/min | ISO 527-2)
    d.a.m. 150 MPa
    Strain at break (5 mm/min | ISO 527-2)
    d.a.m. 3 %
    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m. 76 kJ/m²
  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 225 °C
    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 251 °C
    Temperature of deflection under load HDT/C (8 MPa | ISO 75) 168 °C
    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 262 °C
    Ball pressure test (IEC 60695-10-2) >210 °C
    Temperature index for 50% loss of tensile strength after 5.000h (5.000 h | IEC 60216) 155 °C
    Temperature index for 50% loss of tensile strength after 20.000h (20.000 Std. | IEC 60216) 130 °C
  • Flammability
    Burning rate (UL 94)
    0,4mm Wall thickness V-0 Class
    0,8mm Wall thickness V-0 Class
    1,6mm Wall thickness V-0 Class
    3,2mm Wall thickness V-0 Class
    Burning rate 5V (UL 94)
    1,6mm Wall thickness 5VA Class
    3,2mm Wall thickness 5VA Class
    GWFI (IEC 60695-2-12)
    0,4mm Wall thickness 960 °C
    0,8mm Wall thickness 960 °C
    1,6mm Wall thickness 960 °C
    3,2mm Wall thickness 960 °C
    GWIT (IEC 60695-2-13)
    0,4mm Wall thickness 775 °C
    0,8mm Wall thickness 750 °C
    1,6mm Wall thickness 750 °C
    3,2mm Wall thickness 800 °C
    HWI (UL 746A)
    0,4mm Wall thickness 0 PLC
    0,8mm Wall thickness 0 PLC
    1,6mm Wall thickness 0 PLC
    3,2mm Wall thickness 0 PLC
    HAI (UL 746A)
    0,4mm Wall thickness 0 PLC
    0,8mm Wall thickness 0 PLC
    1,6mm Wall thickness 0 PLC
    3,2mm Wall thickness 0 PLC
    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
    Protection Train (EN 45545-2) R22/R23 HL3
  • General properties
    Density (23°C | ISO 1183) 1,37 g/cm³
  • Electrical Properties
    Comparative tracking index (Test liquid A | IEC 60112) >600 V
    Dieletric strength (3 mm | IEC 60243) 24 kV/mm
    Inclined-Plane Tracking, IPT (ASTM D2303-13) 1 kV
    High voltage tracking rate, HVTR (UL 746A) 0 PLC
  • Rheological Properties
    Flowability (2mm Thickness | AKRO) 460 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.