Preliminary datasheet

PA6 – Polyamide 6 PA6 GF 15

AKROMID® B28 GF 15 2 black (7060)

6100 MPa

  • 6100 MPa

  • 3300 MPa

108 MPa

  • 108 MPa

  • 70 MPa

32 kJ/m²

  • 32 kJ/m²

AKROMID® B28 GF 15 2 black (7060) is a 15% glass fibre reinforced, heat- and UV-stabilised and easy flowing polyamide 6 with average stiffness and strength. This product passed ISO 4892-2 with 1200h exposure time.

Typical applications

Components in mechanical engineering and in the automotive industry

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
6 Drying time 0 - 4 h
Drying temperature (τ ≤ -30°C) 80°C
Processing moisture 0,02 - 0,1%
1 Feed section 60 - 80°C
2 Temperature zone 1 - Zone 4 240 - 290°C
3 Nozzle temperature 260 - 300°C
4 Melt temperature 270 - 290°C
5 Mold temperature 80 - 100°C
P Nach Holding pressure, spec. 300 - 800 bar
P Stau Back pressure, spec. 50 - 150 bar
Injection speed medium to high
Screw speed 8 - 15 m/min
  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 6100 MPa
    conditioned 3300 MPa
    Stress at break (5 mm/min | ISO 527-2)
    d.a.m. 108 MPa
    conditioned 70 MPa
    Strain at break (5 mm/min | ISO 527-2)
    d.a.m. 2,0 %
    conditioned 9 %
    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m. 32 kJ/m²
  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 205 °C
    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 220 °C
    Melting temperature (DSC, 10K/min | DIN EN 11357-1) 222 °C
  • Flammability
    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
  • General properties
    Density (23°C | ISO 1183) 1,24 g/cm³
    Humidity absorption (70°C, 62% r.H. | ISO 1110) 2,6-2,9 %
    Water absorption 23°C saturated (23°C, saturated | ISO 62) 7,7-8,3 %
    Molding shrinkage (flow | ISO 294-4) 0,2-0,4 %
    Molding shrinkage (transverse | ISO 294-4) 0,6-0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

You have questions about our products?

With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.

CONTACT US NOW