AKROMID® B28 GF 30 2 black (7059)

AKROMID® B28 GF 30 2 black (7059) is a 30% glass fiber reinforced, easy flowing polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is UV and heat stabilised and therefore perfectly suitable for technical components in outdoor applications.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

UV-stabilised
easy flow
heat stabilised 130
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 10000 MPa
    conditioned 6500 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 180 MPa
    conditioned 110 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 3 %
    conditioned 4,5 %

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 70 kJ/m²
    conditioned 80 kJ/m²

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 210 °C

    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 220 °C

  • General properties

    Density (23°C | ISO 1183) 1,36 g/cm³

    Molding shrinkage (flow | ISO 294-4) 0,1-0,3 %

    Molding shrinkage (transverse | ISO 294-4) 0,5-0,7 %

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 240 - 290°C

3 Nozzle temperature 260 - 300°C

4 Melt temperature 270 - 290°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.