PA6.6 – Polyamide 6.6 PA66 CF30
AKROMID® A3 CF 30 5 black (7035)
AKROMID® A3 CF 30 5 black (7035) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with high flexural strength and good sliding properties.
This product will be discontinued soon and is replaced by AKROMID® A3 CF 30 5 black (7488) which offers significant mechanical advantages
Mechanically strongly loaded components in all industry sectors
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||260 - 300°C|
|Nozzle temperature||270 - 310°C|
|Melt temperature||280 - 300°C|
|Mold temperature||80 - 100°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 24500 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 250 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 1,5 %
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 52 kJ/m²
Melt temperature (DSC, 10K/min | DIN EN 11357-1) 260 °C
Density (23°C | ISO 1183) 1,26 g/cm³
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
You have questions about our products?
With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.CONTACT US NOW